SYNTHESIS AND CHARACTERIZATION OF A METAL CONTAINING ZEOLITE MATERIAL IN AMMONIUM FLUORIDE MEDIA FOR DRY REFORMING METHANE

SYNTHESIS AND CHARACTERIZATION OF A METAL CONTAINING ZEOLITE MATERIAL IN AMMONIUM FLUORIDE MEDIA FOR DRY REFORMING METHANE. Masters thesis, King Fahd University of Petroleum and Minerals.

[img] PDF
STAMPED=CHEM 610 MS_Thesis_2020 -signed.pdf - Draft Version
Restricted to Repository staff only until 17 May 2021.

Download (4MB)

Arabic Abstract

للتحقيق في دور فلوريد الأمونيوم (NH4F) في توصيف وتوصيف زيوليت ثنائي الأبعاد ZSM-35 المحتوي على المعادن من مورفولوجيا شبيهة بالفيريريت ، قمنا أولاً بتصنيع ZSM-35 في وسط قلوي ثم بعد ذلك بكمية متنوعة من NH4F الوسائط من (0.01g إلى 0.03g). لاحظنا أن درجة التبلور زادت ، تم تعزيز ميزوبوريوسيت كما لوحظ من قاعدة توصيف الأيزوثرمونات بامتصاص N2 على حساب Brunauer-Emmett-Teller (BET) لمنطقة السطح ، تم تغيير حجم البلورة وشكلها. هذه الاتجاهات الملحوظة لها علاقة قوية مع زيادة نسبة F / Si من (0.01 جم إلى 0.03 جم) من NH4F في شكل H– [F] -ZSM-35 وكذلك تناقص حجم البلورة الذي يمكن أن يؤدي إلى الأمل في نانو- حجم الجسيمات ZSM-35 التي لديها إمكانات أكبر كعامل حفاز. مرة أخرى تم العثور على انخفاض الحموضة برونستيد مع زيادة نسبة F / Si من (0.01g إلى 0.03g) من NH4F مقارنة مع ZSM-35 توليفها في وسط قلوية. أيضا دمج المعدنين من المعادن 10 ٪ نيكل (ني) و 1 ٪ الفاناديوم (V) للحصول على NiV-ZSM-35 التي تم اختبار إمكانات الحفز. ومن هنا فإن استخدام فلوريد الأمونيوم (NH4F) في توليف وتوصيف جميع المواد المركبة باستخدام تقنيات التحليل الطيفي والمجهري (XRD ، XRF ، XPS ، FTIR ، و SEM) لمحفز الزيوليت ZSM-35 المحتوي على المعادن في المورفولوجيا ثبت أن خصائص مثل microporosity ، mesoporosity وكذلك الأحجام الجزيئية من هذه المواد الزيوليت يمكن تكييفها لتتناسب مع تطبيق الحفز لدينا غير متجانسة المطلوب.

English Abstract

To investigate the role of ammonium fluoride (NH4F) in the synthesis and characterization of a metal-containing 2D zeolite ZSM-35 of ferrierite-like morphology, we first synthesized ZSM-35 in an alkaline medium and then subsequently in a varied amount of NH4F media from (0.01g to 0.03g). we observed that the degree of crystallinity increased, mesoporosity was enhanced as observed from our N2-adsorption-desorption isotherms characterization base on Brunauer–Emmett–Teller (BET) calculation of the surface area, the crystal size as well as shape were altered. These observed trends have a strong correlation with the increasing F/Si ratio from (0.01g to 0.03g) of NH4F in the form of H–[F]–ZSM-35 as well as decreasing crystal size which can hopefully lead to Nano-particle size ZSM-35 which has even greater potential as a catalyst. Again Brønsted acidity was found to have reduced as the amount of F/Si ratio increase from (0.01g to 0.03g) of NH4F compared the two ZSM-35 synthesized in Alkaline medium. Also bimetallic incorporation of metals 10% Nickel (Ni) and 1% Vanadium (V) to obtain NiV-ZSM-35 whose catalysis potentials was tested. Hence the use of ammonium fluoride (NH4F) media in the synthesis and characterization of all synthesized materials by spectroscopy and microscopy techniques (XRD, XRF, XPS, FTIR, and SEM) of metal-containing ZSM-35 zeolite catalyst of the ferrierite morphology has proven that the properties such microporosity, mesoporosity as well as molecular sizes of these zeolite materials can be tailored to suit our desired heterogeneous catalysis application.

Item Type: Thesis (Masters)
Subjects: Chemistry
Department: College of Chemicals and Materials > Chemistry
Committee Advisor: Adewale, Ganiu Saheed
Committee Members: Alhooshani, Khalid Rasheed and khan, majad
Depositing User: ALHASSAN IBRAHIM (g201706630)
Date Deposited: 03 Jun 2020 12:27
Last Modified: 03 Jun 2020 12:27
URI: http://eprints.kfupm.edu.sa/id/eprint/141568