Studies on catalysts for preferential oxidation of CO in H2-Rich gas mixture

Al-Ghamdi, Musead Salem (2006) Studies on catalysts for preferential oxidation of CO in H2-Rich gas mixture. Masters thesis, King Fahd University of Petroleum and Minerals.

[img]PDF
2141Kb

Arabic Abstract

-

English Abstract

Preferential oxidation is one of the most effective methods for CO clean-up from the reformat stream prior to its introduction in the PEM fuel cell. In this work, Cu-Ce/Y-Al₂O₃ as a base catalyst promoted with Pt and Rh was prepared for the low temperature selective oxidation of CO in hydrogen rich syn gas mixture. Seven catalysts with atomic ratio of 100: 20: 3: 1 for Cu: Ce₂O₃: Pt: Rh were prepared with Cu loading in the range of 0.5 to 6%. Also four catalysts were prepared to investigate the role of Pt and Rh in the catalyst activity. The effects of stoichiometric ratio of O₂/CO and water vapor on the selective oxidation of CO as a function of temperature were investigated. The prepared catalysts were characterized by ICP, Gas Sorption Analyzer, and Temperature Programmed Reduction (TPR). Slight decrease in surface area and pore volume were observed with increasing metal loadings. The TPR results indicate shift towards higher temperature when Pt and Rh were added to Cu-Ce/Y-Al₂O₃ catalyst. Moreover, TPR result showed that there is correlation between reduction temperature and the activity and selectivity of the catalyst. The loading of Cu, Ce, Pt, Rh metals for maximum activity and selectivity were 2.0, 0.657, 0.183, 0.0324 wt % respectively which decreased CO concentration in the product to 4ppm (99.96%). A synergistic effect addition of Pt or/and Rh was observed as an enhancement of the activity and selectivity of the base catalyst (Cu-Ce/Y-Al₂O₃). The CO conversion was increased from 24.7 to 96.77% with addition of 0.183 wt% Pt to the base catalyst. Whereas the addition of 0.0324 Wt% Rh to the base catalyst increased the CO conversion from 24.7 to 44.1%. Addition 10 vol% of water vapor to the feed resulted in higher conversion at lower temperature. The CO conversion was increased whereas the temperature of maximum conversion was decreased by 20℃. Both CO conversion and temperature were reduced when water vapor content in the feed was increased to 20 vol%.



Item Type:Thesis (Masters)
Date:June 2006
Date Type:Completion
Subjects:Chemical Engineering
Divisions:College Of Engineering Sciences > Chemical Engineering Dept
Creators:Al-Ghamdi, Musead Salem
Committee Advisor:Inui, Tomoyuki
Committee Members:Ahmed, Shakeel and Al-Shalabi, M. A.
ID Code:10551
Deposited By:KFUPM ePrints Admin
Deposited On:22 Jun 2008 17:07
Last Modified:30 Apr 2011 15:40

Repository Staff Only: item control page